C95400

✔ STANDARD-STOCKED PRODUCT

  • Product Description: Aluminum Bronze
  • Solids: 1/2" to 9" OD
  • Tubes: 1 1/8" to 9" OD
  • Rectangles: Up to 15"
  • Standard Lengths: 144"
  • Shape/Form: Semi-finished; mill stock or near net shapes; anode; bar stock; billet/bloom; squares; hex; plate; profile or structural shape; flats/rectangular bar
  • Compliance: C95400 is compliant with key legislation including (1) Federal Safe Drinking Water Act 1974 &mdash SDWA, (2) Federal Reduction of Lead in Drinking Water Act 2011 and (3) California AF1953
  • » Download C95400 Spec Sheet (.pdf)

Typical Uses

  • Automotive weld guns
  • Fasteners nuts, large hold down screws
  • Industrial bushings, high strength clamps, gears, valves, bearings, pawl, valve bodies, landing gear parts, worm gears, machine parts, pressure blocks for the steel industry, bearing segments for the steel industry, valve seats, valve guides, pickling hooks, spur gears, heavily loaded worm gears, pump parts
  • Marine covers for marine hardware, ship building
  • Ordnance government fittings
  • Note: Also avilable in heat-treated condition.

Similar or Equivalent Specification

CDA ASTM ASARCON SAE AMS Federal Military Other
C95400 B505       QQ-C-390, G5 MIL-B-16033, CLASS 3 ALUMINUM BRONZE 9C
  B505M       QQ-B-671, CLASS 3    

Chemical Composition (according to ASTM B505/B505M-14)

Cu% Fe% Ni%1 Al% Mn%
Note: Single values represent maximums.
  • 1Ni value includes Co.
  • Note: Cu + Sum of Named Elements, 99.5% min. Single values represent maximums.
83.00 min 3.00-
5.00
 
1.50
10.00-
11.50
 
0.50

Machinability

Copper Alloy UNS No. Machinability Rating Density (lb/in at 68° F)
C95400 60 0.269

Mechanical Properties (according to ASTM B505/B505M-14)

Tensile Strength, min Yield Strength, at .5% extension under load min Elongation, in 2 in. or 50 mm min Brinell Hardness Remarks
ksi MPa ksi MPa % typical BHN  
85 586 32 221 12 170 (3000 kg)  

Physical Properties (provided by CDA)

  US Customary Metric
  • *As Cast, Field Strength 16 kA/m
  • **TQ 50 Temper, Field Strength 16 kA/m
Melting Point - Liquidus 1900° F 1038° C
Melting Point - Solidus 1880° F 1027° C
Density 0.269 lb/in3 at 68° F 7.45 gm/cm3 at 20° C
Specific Gravity 7.45 7.45
Electrical Conductivity 13% IACS at 68° F 0.075 MegaSiemens/cm at 20° C
Thermal Conductivity 33.9 Btu · ft/(hr · ft2 · °F) at 68° F 58.7 W/m at 20° C
Coefficient of Thermal Expansion 9.0 ·10-6 per °F (68°-572° F) 15.5 ·10-6 per °C (20°-300° C)
Specific Heat Capacity 0.1 Btu/lb/°F at 68° F 419.0 J/kg at 293° C
Modulas of Elasticity in Tension 15500 ksi 107000 MPa
Magnetic Permeability* 1.27 1.27
Magnetic Permeability** 1.2 1.2

Fabrication Properties (provided by CDA)

Joining Technique Suitability
Soldering Good
Brazing Good
Oxyacetylene Welding Not Recommended
Gas Shielded Arc Welding Good
Coated Metal Arc Welding Good

Thermal Properties (provided by CDA)

Treatment Temp./Time - US Temp./Time - SI
Stress Temperature 600 316
Solution Minimum 1600 872
Solution Maximum 1675 914
Solution Time 1.0
Solution Medium Water
Precipitation Value    
Precipitation Time  
Precipitation Medium  
Annealing Minimum 1150 622
Annealing Maximum 1225 663
Annealing Time 1.0
Hot Works Minimum    
Hot Works Maximum